SF-1B Bronze Base Bearing for Heavy Machinery and Equipment

SF-1B bronze basic bearing is made of tin bronze as the base, sintered bronze spherical powder in the middle, and rolled PTFE and high temperature resistant filling materials on the surface. It has a high safety factor and is particularly suitable for places where continuous operation cannot be stopped for repairs and places where high temperature cannot be refueled. It has been widely used in the metallurgical steel industry, continuous casting machine billet raceways, high temperature furnace front equipment, cement grouting pumps and screw conveyors. It can be combined with steel sleeves on the outside, or it can be made into flanges to achieve the effect of simultaneous friction of the end face and the inner hole. The sliding part of the bridge support uses SF-1B wear-resistant layer thickened products to replace pure PTFE plates to meet the requirements of 130N/mm2 shaft load.

دریافت یک نقل قول

PREV：SF-1D Hydraulic Special Bearing High-Performance for Hydraulic Systems NEXT：SF-1W Durable Self-Lubricating Lead-Free Bearing Corrosion-Resistant

معرفی محصول
پارامتر
توضیحات مواد
با ما تماس بگیرید

مشخصات محصول

1 می تواند برای مدت طولانی تحت شرایط بدون روغن کار کند.

2 مناسب تر برای شرایط کاری با سرعت کم و بار سنگین، با مقاومت در برابر سایش خوب و اصطکاک بسیار کم

3 مناسب برای شرایطی که تشکیل فیلم روغن دشوار است، مانند رفت و برگشت، چرخش و حرکات متناوب

4 مقاوم در برابر خوردگی و اکسیداسیون.

5 بدون تعمیر و نگهداری و عمر طولانی.

چرا بلبرینگ های بدون روغن را انتخاب کنید؟

کاهش هزینه های تولید

نیازی به دستگاه تامین روغن، سوراخ تزریق روغن یا روغن نیست پردازش شیار، که می تواند تا حد زیادی در هزینه های تولید صرفه جویی کند.

کاهش هزینه های عملیاتی

استفاده از روغن روان کننده را تا حد زیادی کاهش می دهد، تعمیر و نگهداری تجهیزات را کاهش می دهد، و از خطرات پنهان ناشی از عرضه ناکافی نفت جلوگیری کرده و به طور موثر کاهش می دهد هزینه های عملیاتی.

کوتاه کردن زمان طراحی

طراحی بدون روغن ساختار محصول را ساده می کند و به طور موثر در زمان طراحی صرفه جویی می کند. ما حرفه ای هستیم تامین کنندگان ODM SF-1B Bronze Base Bearing for Heavy Machinery and Equipment

منجر به حفاظت از محیط زیست

هیچ بازیافت روغن زباله مورد نیاز نیست، که برای حفاظت از محیط زیست نیز مفید است.

فیلدهای کاربردی

درجه حرارت بالا

· کارخانه فولاد

· کوره ذوب

· تجهیزات خشک کن

· فر پخت

· کنترل کننده حرارت

ضدآب

· دروازه سد

·پمپ آب

· ساختار سوئیچ سیال

· سازه های فراساحلی

· تجهیزات دستگاه داک و سیلت

صنایع شیمیایی

· کارخانه شیمیایی

· تجهیزات آبکاری

· تجهیزات تصفیه فاضلاب

· ماشین آلات رنگرزی

· تجهیزات پالایش نفت و شیمیایی

انرژی

·قدرت باد

· انرژی جدید

کشتی

· جرثقیل عرشه

·لنگر

· روکش دریچه

· بازوی سکان

· ماشین آلات بالابر و تجهیزات حلقه بالابر

خودرو سازی

· قالب مهر زنی

· سازه جوش

· خط نقاشی و خشک کردن

· تسمه نقاله فلزی

·ابزارهای ماشینی

صنعت سنگین

·ماشین آلات کارخانه لوله فولادی

· کارخانه های تایر و کاغذ

· نیروگاه

· ضامن اتصال ماشین آلات تزریق قالب

ساخت و ساز، معدن، بارگیری

· میکسر، آسیاب، پودر

·ماشین آلات ساختمانی

· تجهیزات معدن

· یاتاقان های میله ای اتصال

پل ها و ریل های بالابر

· بلبرینگ پل

· تیرها، پل ها، پل های معلق

· راکتورهای مرتبط با انرژی هسته ای

·ژنراتور بخار

Technical Parameters

●Maximum bearing pressure: 140N/mm2
●Applicable temperature range: -195~+300℃
●Maximum sliding speed: 5m/s
●Friction coefficient: 0.03~0.18
●Maximum allowable PV value (dry): 4.3N/mm2 .m/s
●Maximum allowable PV value (oil): 50N/mm2 .m/s

Metallographic Structure and Material Structure

①Polytetrafluoroethylene and lead mixture 0.01~0.03mm
②Spherical bronze powder 0.2~0.3mm
③Copper back 0.7~2.3mm

Application Features

●The mixture of PTFE and lead can form a good transfer film to protect the grinding shaft during movement.
●The sintered layer and the copper substrate have good thermal conductivity and can quickly transfer the heat generated during operation.
●Copper has self-lubricating properties and can be used in parts that cannot be shut down for maintenance due to long-term operation.
●The base copper has good corrosion resistance and can be used in weak acid and strong alkali situations.
●It has good load-bearing capacity.
●The product has been widely used in the metallurgical steel industry, high-temperature furnace steel ring parts, cement grouting pumps, screw conveyors, port machinery and ship machinery, etc.
●It can be combined with a steel sleeve on the outside; or made into a flange to achieve the effect of using the inner hole and the end face at the same time.

Chemical Properties

Model	Air	Vacuum	Water	Steam	Weak acid	Medium acid	Strong acid	Alkaline solution
SF-1B	good	good	good	good	medium	N/A	N/A	good

MMD-10 End Surface Friction and Wear Test

Model	Test Duration	Test Conditions			Friction Coefficient	Final Temperature	Final Wear Amount
Model	Test Duration	Lubrication Type	Speed	Pressure	Friction Coefficient	(℃)	(mm)
SF-1B	3hr	Dry	0.4m/s	3.5N/mm2	0.151	83	0.014
SF-1B	3hr	Oil	0.4m/s	3.5N/mm2	0.058	55	0.012

ترکیب و خواص مواد
مواد	CuZn25Al5Mn3Fe3	CuSn5Pb5Zn5	CuAl10Ni5Fe5	CuSn12	CuZn25Al5Mn4Fe3
تراکم	8.0	8.9	7.8	8.9	8.0
سختی HB	> 210	> 70	> 150	> 95	> 250
مقاومت کششی N/mm²	> 750	> 200	> 600	> 260	> 800
قدرت تسلیم N/mm²	> 450	> 90	> 260	> 150	> 450
ازدیاد طول %	> 12	> 15	> 10	>	> 800
ضریب بسط خطی 10 ^-5 /℃	1.9	1.8	1.6	1.8	1.9
دمای محدود ℃	-40 تا 300	-40 تا 400	-40 تا 400	-40 تا 400	-40 تا 150
حداکثر بار N/mm²	100	60	50	70	120
حداکثر سرعت (خشک) m/min	15	10	20	10	15
حداکثر PV N/mm²*m/min	200	60	60	80	200
فشرده سازی تغییر شکل دائمی 300N/mm²	<0.01	<0.05	<0.04	<0.05	<0.05
*تقاضای بزرگ با مواد ویژه در دسترس است.

تبادل مواد پایه
کدهای مواد	برندهای چینی GB1176-87	بین المللی ISO 1338	آلمان DIN	ژاپن JIS	آمریکا ASTM(UNS)	انگلستان لیسانس	ایتالیا JM	شرایط قابل اجرا
JDB ریخته گری برنز	ZCuZn25AI5 Fe3Mn3	GCuZn25AI6 Fe3Mn3	DIN1709 G-CuZn25AI5	H5102 CAC304	B30-92 C86300	HTB2	JM18-1	بار بالا، سرعت کم معمولا استفاده می شود
JDB-1برنز	ZCuSn5 Pb5Zn5	GCuPb5 Sn5Zn5	DIN1705 G-CuSn5ZnPb	H5111 BC6	B30-92 C83600	LG2	JM7-15	متوسط بار، سرعت کم معمولا استفاده می شود
JDB-2 برنز	ZCuAI9Fe4 Ni4Mn2	GCuAI10 FeNiS	DIN17656 G-CuAI10Ni	H5114 AIBC3	B30-92 C95500	AB2	JM3-15	بار متوسط، سرعت متوسط، معمولا استفاده می شود
JDB-3 برنز	ZCuSn12		G-CuSn12	CAC503B	B30-92 C90800	PB2	JM1-15	بار متوسط، سرعت کم، معمولا استفاده می شود
JDB-5	ZCuZn25AI6 Fe3Mn3	GCuZn25AI6 Fe3Mn3	DIN1709 G-CuZn25AI5	H5102 CAC304	B30-92 C86300	HTB2	JM18-1	بیش از بار زیاد، سرعت کم، بار زیاد استفاده می شود

روان کننده جامد
روان کننده	امکانات	کاربرد معمولی
SL1 اضافه کردن گرافیت	مقاومت عالی در برابر مواد شیمیایی حملات و اصطکاک کم، حد دمای 400 ℃	کت و شلوار برای ماشین های عمومی و تحت جو
SL4 PTFE اضافه کنید	کمترین اصطکاک و روانکاری آب خوب، حد دمای 300 ℃	کشتی، توربین هیدرولیک، توربین گاز و غیره.

SUBMIT

درباره ما

Zhejiang Mingxu Machinery Manufacturing Co., Ltd. این شرکت که قبلاً به عنوان کارخانه ماشین آلات دقیق Jiashan Mingxu شناخته می شد، در سال 2011 تاسیس شد. این شرکت با موقعیت مکانی و حمل و نقل راحت در منطقه داخلی دلتای رودخانه یانگ تسه واقع شده است. با بیش از ده سال تجربه تولید و تحقیق و توسعه، این شرکت عمیقاً در توسعه و تولید یاتاقان‌های روانکاری جامد، اسکیت‌بردها، لغزنده‌ها و لغزنده‌ها مشارکت داشته است. تامین کنندگان ODM و شرکت JFB بوش شانه فلنج گرافیت منبت کاری یاتاقان خود روان کننده در چین. تولید محصول از تجهیزات اتوماسیون مدرن استفاده می کند، استاندارد سیستم مدیریت کیفیت ISO2000 را به شدت اجرا می کند و فرآیندهای اصلی توسط ماشین های CNC با دقت بالا پردازش می شوند. محصولات اصلی این شرکت مجموعه‌ای از محصولات مانند یاتاقان‌های خود روان‌کار منبت جامد JDB، یاتاقان‌های متخلخل فولاد-مس، یاتاقان‌های خود روان‌شونده SF-1، یاتاقان‌های خود روان‌شونده مرزی SF-2 و یاتاقان‌های مسی FB090 را پوشش می‌دهند. به طور گسترده در صنعت خودرو، ماشین آلات ساختمانی، تجهیزات متالورژی، ماشین آلات معدن، قالب گیری تزریقی، قالب، نساجی، چاپ و بسیاری از زمینه های تولید ماشین آلات استفاده می شود. تاکنون محصولات این شرکت در سراسر چین گسترش یافته و به بسیاری از کشورهای خارجی صادر شده است و عمیقاً مورد توجه مشتریان داخلی و خارجی قرار گرفته است. Mingxu Machinery به اصل خدمات "خدمات با کیفیت بالا با کیفیت" پایبند است و تلاش می کند محصولات و خدمات حرفه ای را به مشتریان ارائه دهد. عرضه عمده فروشی MXB-JFB بوش شانه فلنج گرافیت منبت کاری خود روان کننده بلبرینگ. این شرکت به معرفی استعدادها، بهبود مکانیسم مدیریت، یکپارچگی، توسعه، نوآوری و تلاش برای ایجاد یک برند در سطح جهانی ادامه خواهد داد.